Enhancing Ultra-violet Optical Properties of Aluminum Mirrors with a Single Step Approach to Oxide Removal and Fluorine Passivation
(Room Room 104-C)
29 Apr 19
9:20 AM
-
9:40 AM
Astronomical measurements in the Far Ultra-violet (FUV, 90-200nm) require the use of aluminum thin films due to aluminum’s high reflectivity over this wavelength range. Unfortunately, the native aluminum oxide layer formed in atmosphere is strongly absorbing in this wavelength range, requiring that the aluminum films be passivated with a dielectric that inhibits oxidation. Due to the fast oxidation of aluminum, a simultaneous etch and deposition process is desirable to both eliminate the native aluminum oxide after growth and replace it with a different passivation coating layer. Optical measurements in the FUV range are some of the most challenging due to limited selection of low reflectivity coatings available for use on aluminum thin films. Typically magnesium fluoride (MgF2) or lithium fluoride (LiF) coatings are used for these passivation purposes but each has its problems. MgF2 has an absorption cutoff at 115 nm occluding a critical part of the FUV spectrum. LiF has a lower absorption cutoff at 102.5 nm, but is hygroscopic and thus susceptible to degradation in ambient conditions. A promising alternative to these coating materials is AlF3, which theoretically can provide reflectivity greater than 50% down to 100 nm if the coating is sufficiently thin. In this work, we explore the use of electron beam generated plasmas to simultaneously etch the native oxide layer from aluminum thin films while depositing an AlF3 capping layer to passivate the aluminum reflector. XPS measurements indicate that this approach is cable of producing very thin (<5 nm) AlF3 films with some mild oxygen contamination. We will discuss the impact of plasma power, chemistry, and time on the composition and structure of the passivating layer and its subsequent optical properties. This work is partially supported by the Naval Research Laboratory base program.